• Lowest Price for Erbium,Chromium Doped Yttrium Scandium Gallium Garnet - ZnGeP2 Crystals – Dien

    Lowest Price for Erbium,Chromium Doped Yttrium Scandium Gallium Garnet - ZnGeP2 Crystals – Dien

    ZGP crystals possessing large nonlinear coefficients (d36=75pm/V), wide infrared transparency range(0.75-12μm), high thermal conductivity(0.35W/(cm·K)), high laser damage threshold (2-5J/cm2)and well machining property, ZnGeP2 crystal was called the king of infrared nonlinear optical crystals and is still the best frequency conversion material for high power, tunable infrared laser generation. We can offer high optical quality and large diameter ZGP crystals with extremely low absorption coef...
  • Trending Products  E-O Q-Switchs - Nd:YAP Crystals – Dien

    Trending Products E-O Q-Switchs - Nd:YAP Crystals – Dien

    Nd:YAP  AlO3 perovskite (YAP) is a well known host for solid state lasers. The crystal anisotropy of YAP offers numerous advantages.It permits a small tuning of wavelength by varyingthe wave vector direction in the crystal. Furthermore, the output beam is linearly polarised. Advantages of Nd:YAP Crystals: Comparable threshold and slope efficiency at 1079nm to Nd:YAG at 1064nm Higher efficiency at 1340nm compared to Nd:YAG at 1319nm Linearly polarized output beam Higher absorption in water and...
  • Chinese Professional Crystal – TSAG crystal – Dien

    Chinese Professional Crystal – TSAG crystal – Dien

    TSAG Faraday crystal is an ideal magneto-optical crystal, which is mainly used in the wavelength range of 400-1600 nanometers, namely the visible and infrared bands. TSAG is an indispensable crystal for the next generation of high-power lasers due to its advantages of high constant, good thermal and mechanical properties. Compared with TGG, the Verdet constant at 1064 nm of TSAG is 20 % higher and the absorption is 30 % lower. Recently, the optical and scintillation properties of TSAG (Tb3Sc2...
  • Chinese Professional Yb Yag - LGS Crystals – Dien

    Chinese Professional Yb Yag - LGS Crystals – Dien

    La3Ga5SiO14 crystal (LGS crystal) is an optical nonlinear material with high damage threshold, high electro-optical coefficient and excellent electro-optical performance. LGS crystal belongs to trigonal system structure, smaller thermal expansion coefficient, thermal expansion anisotropy of crystal is weak, the temperature of the high temperature stability is good (better than SiO2), with two independent electro – optical coefficients are as good as those of BBO Crystals. The electro-op...
  • Good Wholesale Vendors  Nd:Yvo4 - BaGa4Se7 Crystals – Dien

    Good Wholesale Vendors Nd:Yvo4 - BaGa4Se7 Crystals – Dien

    High-quality crystals of BGSe (BaGa4Se7) is the selenide analogue of the chalcogenide compound BaGa4S7, whose acentric orthorhombic structure was identified in 1983 and the IR NLO effect was reported in 2009, is a newly developed IR NLO crystal. It was obtained via the Bridgman–Stockbarger technique. This crystal exhibits high transmittance over the wide range of 0.47–18 μm, except for an absorption peak at around 15 μm. The FWHM of the (002) peak rocking curve is about 0.008° and the transmi...
  • Factory supplied Nd Yag Rod - CaF2 Windows – Dien

    Factory supplied Nd Yag Rod - CaF2 Windows – Dien

    ZnS is a very important optical crystals applied in IR waveband. Transmitting range of CVD ZnS is 8um-14um, high transmittance, low absorption, ZnS with multi-spectrum level by heating etc. static pressure technics has improved the transmittance of IR and visible range. Zinc Sulphide is produced by synthesis from Zinc vapour and H2S gas, forming as sheets on Graphite susceptors. Zinc Sulphide is microcrystalline in structure, the grain size being controlled to produce maximum strength. Multis...